| Customization: | Available |
|---|---|
| Surface Finishing: | Coating |
| Panel Thickness: | 5mm |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Aluminum Composite material Use for Wall Cladding Decoration
1)Material
A) Front : aluminium alloy sheet coated fluoro-carbon resin (PVDF) with Nano lacquer
B) Core: nontox low density polyethylene
C) Back: aluminium alloy sheet coated with polyester resin painting
D) Surface coating thickness: 32μ±1μ
E) Aluminium alloy: 3003 H24
F) Sheet thickness: 0.3mm,0.4mm,0.5mm
2)Dimensions
A) Thickness: 3mm,4mm,6mm,8mm,10mm
B) Width: 1220mm,1250mm,1500mm,1570mm,1800mm,2000mm(max)
C) Length: 2440mm,3050mm,3200mm( max:6000mm)
D) Weight: 5.5kg/sqm baesd on 0.5/4mm thickness
E) Standard size:1220*2440mm
F) Qty/20'fcl:4mm/2380sqm; 3mm/2977sqm
G) Non-stanard size are available according to requirement
3)Standard
A) West Europe standard ( Germany DIN Standard);
B) The EAST Europe standard ( Russian standard );
C) The commonweathlth standard (U.K BS Standard );
D) The North America ASTM standard;
4)Features
A) Light weight,flat surface and high strength
B) Excellent heat insulation ,sound insulation,fire-resistance,acid-resistance,alkali-resistance,weatherproofness and non-resonance
C) Various uniform colors
D) Rbright ,elegan and magnificent,fit for various designs
E) Kynar 500 PVDF resin feature strong chemical resistance,unique colors can be easily maintained
5)Applications
A) May be widly used in gallaies,exhibition,saloons,stores,offices,banks,hotels,restaurants and apartments
B) An ideal decorative materials for buildings
C) An ideal outer and inner walls
D) Kitchen cabinees,billboards,signboards,tunnels,subway,interiors
E) Cellings,eaves,galleries,balconies,partitions,interior decorations
F) Telephone tooths,vehicle bodies,yachts,industrial usage etc.
6)Alubang® ACP compared with solid aluminium: Required thickness and actual weights of panels with same rigidity
| Alubang® ACP | Aluminium | ||||
| Rigidity (E J) | Section modulus | Thickness | Weight | Thickness | Weight |
| 1250 kN cm2/m | 1.25 cm3/m | 3 mm | 4.5kg/m2 | 2.7 mm | 7.3kg/m2 |
| 2400 kN cm2/m | 1.75 cm3/m | 4 mm | 5.5kg/m2 | 3.3 mm | 8.9kg/m2 |
7)Alubang ACP Tolerance(mm)
| Thickness | ± 0.2 |
| Width | ± 2 |
| Length | ± 4 |
| Diagonal | ± 5 |
8)Alubang ACP Physical Properties for Panel
| Panel density | 5.5kg/m2 |
| Peel Strength | Average 7.0 N/mm |
| Tensile Strength | 52.5 Mpa |
| Flexural Strength | 100.0 Mpa |
| Shear Strength | 28.1 Mpa |
9)Physical properties for aluminium and coating
| Aluminium alloy | 1100, 3003, 5005 |
| Pencil hardness | 2H |
| Toughness of coating | 2T |
| Elongation | 5% |
| Tensile strength | 130 Mpa |
| Temperature Resistance | -50°C to +90°C |
| Impact Strength | 50kg/cm2 , no change |
| Boiling water resistance | Boiling for 2 hrs, no change |
| Thermal Expansion | 2.4mm/m at 100°C Temp difference |
| Acid Resistance | Immersed in 2% HC1 for 24 hrs, no change |
| Alkali Resistance | Immersed in 2% NaOH for 24 hrs, no change |
| Cleaning Resistance | Cleaned 1000 times with water, no change |
| Oil Resistance | Immersed in 20# engine oil for 24 hrs, no change |
| Solvent Resistance | Cleaned 100 times with dimethylbenzene, no change |